Fused Silica With Grooves – Fused Silica (CTE 0.55 x 10^-6 /K, 185 nm – 2.5 um); depth from 0.2 mm, V, U or square section. No minimum order; DFM review included with every RFQ.
Buyers come to fused silica with grooves with two kinds of parts: catalog-adjacent blanks that need accurate finishing, and genuinely custom geometry. We quote both from the same dataset – JGS1 (UV), JGS2 (standard), JGS3 (IR) stock in 0.10 – 50 mm, blanks to 450 x 450 mm.
Key parameters
| Material | Fused Silica (JGS1 (UV), JGS2 (standard), JGS3 (IR)) |
|---|---|
| Thermal expansion (CTE) | 0.55 x 10^-6 /K |
| Service temperature | 1,100 C continuous |
| Transmission range | 185 nm – 2.5 um |
| Density | 2.20 g/cm3 |
| Knoop hardness | 500 kg/mm2 |
| Refractive index | 1.458 @ 587 nm |
| Stock thickness | 0.10 – 50 mm |
| Maximum blank size | 450 x 450 mm |
| Feature | Grooves |
| Capability | depth from 0.2 mm, V, U or square section |
| RFQ inputs | PDF/DXF/STEP drawing, quantity brackets, surface and edge spec |
Specification advice
The shop-floor rules that matter here:
- Material note: its hardness and brittleness demand diamond tooling and controlled feeds.
- Feature rule: depth under 50% of thickness preserves strength.
- Over-specification is the quiet budget killer: a 20/10 scratch-dig face costs roughly three times an 80/50 face, so grade each surface individually.
For the complete framework, see the tolerance design guide and the holes and edges design guide.
Process window
Beyond this page, Fused Silica routinely runs through lapping, laser cutting, grinding, etching in our shop – most real parts combine two or three of these steps.
These features are produced by cnc machining or ultrasonic machining. Capability: depth from 0.2 mm, V, U or square section. Design rule worth copying onto the drawing: depth under 50% of thickness preserves strength.
Who orders this
The recurring buyers of fused silica with grooves: ccd inspection equipment (CCD cover plates, reference grids, stage glass); microfluidic devices (chips, manifolds, via plates, bonded stacks); machine vision (camera windows, ring-light diffusers, calibration plates). Background reading on the underlying material science: RP Photonics: fused silica.
The fastest route to a quote is geometry: use the 3D builder below, draw a dimensioned 2D drawing from it, or open the site-wide custom glass machining 3D + 2D builder for fully custom parts.
Engineers scoping this work usually also review wafer dicing process, fused silica wafers 2-12 inch, holes and edges design guide.
Buyer questions, answered
Is there a minimum order for fused silica with grooves?
No. Single prototypes are accepted, and pricing steps down at 10, 100 and 1,000 pieces.
How fast can prototypes ship?
Machined prototypes ship in 5 – 10 working days. Coated or bonded parts add 1 – 2 weeks depending on queue slots.
What files do you need for a quote?
A dimensioned PDF plus DXF or STEP geometry. If only a sketch exists, our drawing review service formalizes it before quoting.
Do parts ship with inspection data?
Dimensional reports, surface certificates and material certs per melt are available; specify the level on the RFQ.
Specifications on this page were last reviewed by our engineering team in September 2026.