Quick answer: Grinding Borosilicate Glass covers Borosilicate Glass (CTE 3.3 x 10^-6 /K, 360 nm – 2.0 um); Grinding to flatness to 5 um over 100 mm. Prototypes ship in 5-10 working days.
The combination of Borosilicate Glass and Grinding comes up constantly in RFQs for a reason – the material offers thermal shock resistance, and Grinding is the right way to get accurate geometry into it. Expect flatness to 5 um over 100 mm and Ra 0.2 – 0.8 um.
The numbers
| Material | Borosilicate Glass (3.3 expansion group per ISO 3585) |
|---|---|
| Thermal expansion (CTE) | 3.3 x 10^-6 /K |
| Service temperature | 450 C continuous |
| Transmission range | 360 nm – 2.0 um |
| Density | 2.23 g/cm3 |
| Knoop hardness | 480 kg/mm2 |
| Refractive index | 1.473 @ 587 nm |
| Stock thickness | 0.50 – 30 mm |
| Maximum blank size | 600 x 400 mm |
| Process | Grinding |
| Working tolerance | flatness to 5 um over 100 mm |
| Minimum feature | thickness to +/-0.005 mm |
| Surface finish | Ra 0.2 – 0.8 um |
| Thickness window | 0.3 – 60 mm |
| Edge condition | ground perimeter, squareness 0.02 mm |
| RFQ inputs | PDF/DXF/STEP drawing, quantity brackets, surface and edge spec |
DFM notes from the shop floor
Before sending the RFQ, check these against your drawing:
- Material note: sheet stock carries more thickness variation than float wafer stock, so lapping is often the first step.
- Process boundary: subsurface damage of 5 – 15 um must be budgeted and removed by polishing on optical faces.
- Over-specification is the quiet budget killer: a 20/10 scratch-dig face costs roughly three times an 80/50 face, so grade each surface individually.
The full rules live in our tolerance design guide and holes and edges design guide.
What the process holds
Grinding earns its place through bringing thickness, flatness and parallelism into calibrated tolerance before polish. Its boundary condition – subsurface damage of 5 – 15 um must be budgeted and removed by polishing on optical faces – is the first thing our DFM review checks.
Beyond this page, Borosilicate Glass routinely runs through cnc machining, double-side polishing, lapping, drilling in our shop – most real parts combine two or three of these steps.
Who orders this
Orders for grinding borosilicate glass cluster in medical diagnostics (flow cells, slides, microplate bottoms, cuvette windows); scientific instruments (reference flats, cells, prism mounts, stage inserts); laboratory instruments (cuvettes, sight glasses, stir-cell windows). Background reading on the underlying material science: ISO 3585 borosilicate glass 3.3.
The fastest route to a quote is geometry: use the 3D builder below, draw a dimensioned 2D drawing from it, or open the site-wide custom glass machining 3D + 2D builder for fully custom parts.
Related reading on this site: precision glass grinding, material selection guide, holes and edges design guide.
Buyer questions, answered
What equipment runs the grinding work?
Rotary surface grinders and double-disc machines with diamond wheels.
Is there a minimum order for grinding borosilicate glass?
No. Single prototypes are accepted, and pricing steps down at 10, 100 and 1,000 pieces.
How fast can prototypes ship?
Machined prototypes ship in 5 – 10 working days. Coated or bonded parts add 1 – 2 weeks depending on queue slots.
What files do you need for a quote?
A dimensioned PDF plus DXF or STEP geometry. If only a sketch exists, our drawing review service formalizes it before quoting.