Edge Grinding D263 Thin Glass – D263 Thin Glass (CTE 7.2 x 10^-6 /K, 350 nm – 2.0 um); Edge Grinding to chamfer +/-0.05 mm. No minimum order; DFM review included with every RFQ.
Ask any process engineer what makes d263 thin glass difficult and the answer is specific: ultra-thin stock cannot take conventional clamping; parts are machined on wax or UV-tape carriers. Our edge grinding line is tooled around exactly that – CNC edge grinders with profiled diamond wheels – holding chamfer +/-0.05 mm on parts from 0.1 – 25 mm thick.
Specification envelope
| Material | D263 Thin Glass (SCHOTT D 263 T eco) |
|---|---|
| Thermal expansion (CTE) | 7.2 x 10^-6 /K |
| Service temperature | 400 C (Tg 557 C) |
| Transmission range | 350 nm – 2.0 um |
| Density | 2.51 g/cm3 |
| Knoop hardness | 590 kg/mm2 |
| Refractive index | 1.523 @ 587 nm |
| Stock thickness | 0.03 – 1.1 mm |
| Maximum blank size | 440 x 360 mm |
| Process | Edge Grinding |
| Working tolerance | chamfer +/-0.05 mm |
| Minimum feature | 0.1 mm chamfer leg |
| Surface finish | ground C or R profile, polish option |
| Thickness window | 0.1 – 25 mm |
| Edge condition | C-chamfer, R-round, pencil or OG profile |
| RFQ inputs | PDF/DXF/STEP drawing, quantity brackets, surface and edge spec |
Manufacturing capability
The core strength of Edge Grinding is edge strength – a finished chamfer roughly doubles the bend strength of a cut edge. The honest limit: profiles below 0.1 mm leg length are lapped by hand and priced per edge. Both belong on the drawing before quoting, not after.
One material, many routes: on D263 Thin Glass we also quote laser cutting, grinding, cnc machining, and multi-step drawings are the norm rather than the exception.
Design guidance
Before sending the RFQ, check these against your drawing:
- Material note: ultra-thin stock cannot take conventional clamping; parts are machined on wax or UV-tape carriers.
- Process boundary: profiles below 0.1 mm leg length are lapped by hand and priced per edge.
- Over-specification is the quiet budget killer: a 20/10 scratch-dig face costs roughly three times an 80/50 face, so grade each surface individually.
The full rules live in our tolerance design guide and holes and edges design guide.
Who orders this
edge grinding d263 thin glass shows up across oled packaging (cover lids, frit-seal frames, fill-port plates); microfluidic devices (chips, manifolds, via plates, bonded stacks); led packaging (groove covers, phosphor carriers, package windows). Background reading on the underlying material science: SCHOTT D 263 thin glass.
Dimensions still moving? Configure this part live in the 3D builder below, or open the full custom glass machining 3D builder to start from a blank canvas.
Useful companion pages: edge grinding overview, holes and edges design guide, glass wafer bonding.
Buyer questions, answered
What tolerances are achievable on D263 Thin Glass parts?
Ground features hold +/-0.01 mm and lapped thickness reaches +/-0.003 mm. Ultra-thin stock cannot take conventional clamping; parts are machined on wax or UV-tape carriers.
What thickness range do you stock for D263 Thin Glass?
Standard stock spans 0.03 – 1.1 mm, with blanks up to 440 x 360 mm. Other formats are sourced per order.
How does D263 Thin Glass behave under heat?
CTE is 7.2 x 10^-6 /K and continuous service reaches 400 C (Tg 557 C), which is what drives its use where down-drawn fire-polished surfaces matters.
What accuracy does edge grinding hold?
Chamfer +/-0.05 mm with minimum features of 0.1 mm chamfer leg. Profiles below 0.1 mm leg length are lapped by hand and priced per edge.