AR Coating JGS1 Quartz Glass – JGS1 Quartz Glass (CTE 0.55 x 10^-6 /K, 185 nm – 2.5 um (UV grade)); R < 0.5% per face, 400 – 700 nm (custom bands 193 nm – 2 um). No minimum order; DFM review included with every RFQ.
Specify ar coating jgs1 quartz glass when the bare substrate falls short: anti-reflective multilayer, processed by ion-assisted e-beam deposition, brings JGS1 Quartz Glass to R < 0.5% per face, 400 – 700 nm (custom bands 193 nm – 2 um).
Specification envelope
| Material | JGS1 Quartz Glass (UV-grade synthetic, bubble class 0) |
|---|---|
| Thermal expansion (CTE) | 0.55 x 10^-6 /K |
| Service temperature | 1,100 C continuous |
| Transmission range | 185 nm – 2.5 um (UV grade) |
| Density | 2.20 g/cm3 |
| Knoop hardness | 500 kg/mm2 |
| Refractive index | 1.458 @ 587 nm |
| Stock thickness | 0.10 – 30 mm |
| Maximum blank size | 300 mm diameter |
| Treatment | AR Coating – anti-reflective multilayer |
| Specification | R < 0.5% per face, 400 – 700 nm (custom bands 193 nm – 2 um) |
| Deposition / method | ion-assisted e-beam deposition |
| RFQ inputs | PDF/DXF/STEP drawing, quantity brackets, surface and edge spec |
What the process holds
Beyond this page, JGS1 Quartz Glass routinely runs through double-side polishing, laser cutting, edge grinding, drilling in our shop – most real parts combine two or three of these steps.
Specification advice
Before sending the RFQ, check these against your drawing:
- Material note: UV-grade surfaces must be polished without subsurface damage that scatters below 250 nm.
- Sequence matters: all machining happens before ar coating; post-coating rework is not economical.
- Over-specification is the quiet budget killer: a 20/10 scratch-dig face costs roughly three times an 80/50 face, so grade each surface individually.
For the complete framework, see the tolerance design guide and the holes and edges design guide.
Where these parts end up
The recurring buyers of ar coating jgs1 quartz glass: laser systems (windows, beam splitters, debris shields); aerospace optics (sensor windows, star-tracker flats, radiation-tolerant ports). Background reading on the underlying material science: RP Photonics: fused silica.
The fastest route to a quote is geometry: use the 3D builder below, draw a dimensioned 2D drawing from it, or open the site-wide custom glass machining 3D + 2D builder for fully custom parts.
Engineers scoping this work usually also review high-temperature quartz windows, CNC machining capability, tolerance design guide.
Frequently asked questions
How does JGS1 Quartz Glass behave under heat?
CTE is 0.55 x 10^-6 /K and continuous service reaches 1,100 C continuous, which is what drives its use where deep-UV transmission to 185 nm matters.
What does ar coating add?
Raises transmission from ~92% to above 99%. Applied by ion-assisted e-beam deposition to R < 0.5% per face, 400 – 700 nm (custom bands 193 nm – 2 um).
Is there a minimum order for ar coating jgs1 quartz glass?
No. Single prototypes are accepted, and pricing steps down at 10, 100 and 1,000 pieces.
How fast can prototypes ship?
Machined prototypes ship in 5 – 10 working days. Coated or bonded parts add 1 – 2 weeks depending on queue slots.
Specifications on this page were last reviewed by our engineering team in August 2026.