Edge Grinding JGS2 Quartz Glass: JGS2 Quartz Glass (CTE 0.55 x 10^-6 /K, 220 nm – 2.5 um); Edge Grinding to chamfer +/-0.05 mm. Single-piece prototypes to production volumes, quoted from your drawing.
The combination of JGS2 Quartz Glass and Edge Grinding comes up constantly in RFQs for a reason – the material offers lower oh than jgs1, and Edge Grinding is the right way to get accurate geometry into it. Expect chamfer +/-0.05 mm and ground C or R profile, polish option.
The numbers
| Material | JGS2 Quartz Glass (Optical grade, bubble class 1) |
|---|---|
| Thermal expansion (CTE) | 0.55 x 10^-6 /K |
| Service temperature | 1,100 C continuous |
| Transmission range | 220 nm – 2.5 um |
| Density | 2.20 g/cm3 |
| Knoop hardness | 500 kg/mm2 |
| Refractive index | 1.458 @ 587 nm |
| Stock thickness | 0.20 – 40 mm |
| Maximum blank size | 300 mm diameter |
| Process | Edge Grinding |
| Working tolerance | chamfer +/-0.05 mm |
| Minimum feature | 0.1 mm chamfer leg |
| Surface finish | ground C or R profile, polish option |
| Thickness window | 0.1 – 25 mm |
| Edge condition | C-chamfer, R-round, pencil or OG profile |
| RFQ inputs | PDF/DXF/STEP drawing, quantity brackets, surface and edge spec |
DFM notes from the shop floor
Three items decide most of the cost and lead time on this work:
- Material note: thicker blanks need stress-relief annealing before tight-flatness grinding.
- Process boundary: profiles below 0.1 mm leg length are lapped by hand and priced per edge.
- Over-specification is the quiet budget killer: a 20/10 scratch-dig face costs roughly three times an 80/50 face, so grade each surface individually.
The full rules live in our tolerance design guide and holes and edges design guide.
Manufacturing capability
The core strength of Edge Grinding is edge strength – a finished chamfer roughly doubles the bend strength of a cut edge. The honest limit: profiles below 0.1 mm leg length are lapped by hand and priced per edge. Both belong on the drawing before quoting, not after.
One material, many routes: on JGS2 Quartz Glass we also quote ultrasonic machining, polishing, laser cutting, etching, and multi-step drawings are the norm rather than the exception.
Where these parts end up
edge grinding jgs2 quartz glass shows up across led packaging (groove covers, phosphor carriers, package windows); industrial displays (touch covers, gauge windows, printed bezels); machine vision (camera windows, ring-light diffusers, calibration plates). Background reading on the underlying material science: ScienceDirect: fused quartz.
The fastest route to a quote is geometry: use the 3D configurator below, or the site-wide custom glass machining 3D builder for fully custom parts.
Engineers scoping this work usually also review edge grinding overview, fused silica wafers 2-12 inch, holes and edges design guide.
Frequently asked questions
What tolerances are achievable on JGS2 Quartz Glass parts?
Ground features hold +/-0.01 mm and lapped thickness reaches +/-0.003 mm. Thicker blanks need stress-relief annealing before tight-flatness grinding.
What thickness range do you stock for JGS2 Quartz Glass?
Standard stock spans 0.20 – 40 mm, with blanks up to 300 mm diameter. Other formats are sourced per order.
How does JGS2 Quartz Glass behave under heat?
CTE is 0.55 x 10^-6 /K and continuous service reaches 1,100 C continuous, which is what drives its use where visible and near-IR clarity matters.
What accuracy does edge grinding hold?
Chamfer +/-0.05 mm with minimum features of 0.1 mm chamfer leg. Profiles below 0.1 mm leg length are lapped by hand and priced per edge.
Specifications on this page were last reviewed by our engineering team in July 2026.